High Cr Cast Iron Jaw Plates Crusher Wear Parts With More Than HRC60 Hardness

High Cr Cast Iron Jaw Plates Crusher Wear Parts With More Than HRC60 Hardness

Brand Name:Chen‘s Liner
Certification:ISO 9001:2008
Model Number:DF143
Minimum Order Quantity:5 Ton/Tons
Delivery Time:It depends on the quantity to be ordered.
Payment Terms:L/C,T/T
Contact Now

Add to Cart

Active Member
Location: Wuxi Jiangsu
Address: Zhongyao,Xishan District, Wuxi, 214000, Jiangsu, China
Supplier`s last login times: within 32 hours
Shipping
lt's easy to get a shipping quote! Just click the button below and complete the short form.
Get Shipping Quote
Product Details Company Profile
Product Details

High Cr Cast Iron Jaw Plates Crusher Wear Parts With More Than HRC60 Hardness


Quick Details

1. Alloy: 15%Cr

2. Hardness: ≥HRC60;

3. Microstructure:Fine Martensite + Carbide + retained Austenite(≤6%)


High Cr Cast Iron Jaw Plates

1. Alloy: 15%Cr.
2. The Jaw Plates are cleaned, sandblasted with a nice surface without any obvious visual defects that can avoid the normal working of the castings.

3. Hardness: more than HRC60;

4. Microstructure: Fine Martensite + Carbide + retained Austenite(≤6%)


In the recent 20 years, our liners have been widely used in large, medium and small ball mills in Chinese power generation, mining, cement, Chemical engineering and metallurgical industries and super fine pulverizing equipments. It is the only recommended liner product in the latest standard of the electric-power industry in China.


Technical Parameters

Wuxi Orient Anti-wear Engineering Co., Ltd.

Chemical Composition & Mechanical Property of Wear-resistant Castings

Item

Cr-Mo

Alloy Steel I

Cr-Mo

Alloy Steel II

Cr-Mo

Alloy Steel III

High Cr white iron

High Cr Alloy Steel

High Manganese Steel

Ni-Hard cast iron

C

0.30~0.50

0.65~0.90

0.40~0.90

2.40~3.20

1.1~2.2

0.90~1.30

2.40~3.60

Si

0.50~1.20

≤0.75

0.70~1.20

0.60~1.20

0.60~1.20

≤0.08

≤0.80

Mn

0.40~1.20

0.50~1.20

0.60~1.00

0.50~1.00

0.50~1.00

11.00~18.00

≤2.0

Cr

1.70~2.50

1.50~2.50

4.00~7.00

12.00~30.00

11.00~30.00

1.50~2.50

1.5~10

S

≤0.04

≤0.06

≤0.04

≤0.04

≤0.04

≤0.04

≤0.15

P

≤0.04

≤0.06

≤0.06

≤0.06

≤0.06

≤0.06

≤0.15

Mo

≤0.5

≤0.5

≤0.5

0.10~3.0

0.10~3.0

≤1.0

≤0.10

Cu

0.10~0.60

≤0.25

0.20~0.40

0.10~1.00

0.10~1.00

-

-

Ni

≤0.50

≤0.30

0~0.30

0~0.30

0~0.30

-

3.3~10

Re

≤0.02

≤0.02

≤0.02

-

-

-

-

Equivalent

Specifications

DL/T 681-1999


GB/T26651-2011

AS 2074 L2B Mod

DL/T 681-1999

GB/T 8263-1999

AS 2027 Cr27

AS 2027 CrMo 15/3

AS 2027 CrMo 20/2/1

ASTM A532 Class III type A 25% Cr

ASTM A532Class II type B 15% Cr-Mo

BS 4844 3E

DIN1695

NFA32401.

GB/T 5680-1998

DL/T 681-1999

JIS G 5153-1999

ASTM A 128

DIN GX120Mn12

AFNOR:Z120Mn12

GB/T 8263-1999

AS 2027/Ni-Cr1-550

AS 2027/Ni-Cr2-500

AS 2027/Ni-Cr4-500

AS 2027/Ni-Cr4-600

AS 2027/Ni-Cr4-630

ASTM A 532 1-A,B,C,D

ASTM A 532 2-A,B,C,D,E

ASTM A 532 3-A

Material Type

Martensite Steel

Martensite or

Pearlitic Cr Mo Steel

Martensite Steel

Martensite matrix

Austenitic Mn Steel

-

Hardness

HRc≥48

HB470 &

HB 321~370

HRc≥50

HRc≥56

HB≤300

HRc≥56

Impact Value

Ak≥40J

-

Ak≥10J

Ak≥4J

Ak≥80J

-


Our foundry has complete melting, heat treatment and test equipments, such as mid-frequency induction electrical furnaces, quenching and tempering furnaces, blast shot, spectrometer, Rockwell and Brinell Hardness tester, impactor, UT tester and metallographic microscope. We achieved the certificate of quality management system ISO 9001:2008. We have been exporting castings to oversea markets, such as Brazil, Australia and South Africa.


China High Cr Cast Iron Jaw Plates Crusher Wear Parts With More Than HRC60 Hardness supplier

High Cr Cast Iron Jaw Plates Crusher Wear Parts With More Than HRC60 Hardness